Polypropylene-based material with high impact and compression strength with greater than 100% elongation at break. Ideal for fixtures and tooling. This resin allows production of functional parts that require high stiffness with good surface finish and high impact resistance.
Benefits:
- Tough and Durable
- Superior Impact Strength
- Nice Surface Finish, Machinable
Ideal for:
- Manufacturing aids / jigs & fixtures
- Housings
- Insoles
Physical Properties
Tensile Strength at Break
40 ± 2.3 MPa
Young's Modulus
1,550 ± 74 MPa
Elongation at Failure
110.8 ± 9%
Flexural Stress at Yield
57.8 ± 2.7 MPa
Flexural Modulus
1,365 ± 15.7 MPa
Flexural Strain at Break
>10%
IZOD Impact Strength (Notched)
55.2 ± 5 J/m
HDT @ 0.455 MPA (VICAT)
52°C
Shore Hardness D
88
Water Absorption
1.2%