3D Bioplotter Research Papers

A promising alternative to current treatment options for degenerative conditions of the temporomandibular joint (TMJ) is cartilage tissue engineering, using 3D printed scaffolds and mesenchymal stem cells. Gelatin, with its inherent biocompatibility and printability has been proposed as a scaffold biomaterial, but because of its thermoreversible properties, rapid degradation and inadequate strength it must be crosslinked to be stable in physiological conditions. The aim of this study was to identify non-toxic and effective crosslinking methods intended to improve the physical properties of 3D printed gelatin scaffolds for cartilage regeneration. Dehydrothermal (DHT), ribose glycation and dual crosslinking with both DHT and…

We present a solution to regenerate adipose tissue using degradable, soft, pliable 3D-printed scaffolds made of a medical-grade copolymer coated with polydopamine. The problem today is that while printing, the medical grade copolyesters degrade and the scaffolds become very stiff and brittle, being not optimal for adipose tissue defects. Herein, we have used high molar mass poly(L-lactide-co-trimethylene carbonate) (PLATMC) to engineer scaffolds using a direct extrusion-based 3D printer, the 3D Bioplotter®. Our approach was first focused on how the printing influences the polymer and scaffold’s mechanical properties, then on exploring different printing designs and, in the end, on assessing surface…

Synthetic polycaprolactone (PCL) was modified with various concentrations of gelatin (GL) to enhance its physical properties and biological activity for bone regeneration. A novel trisolvent mixture has been used to mix PCL and GL that were fabricated as scaffolds using 3D plotting. The scaffolds were characterized for their mechanical properties, hydrophilicity and swelling ability. In addition, the structure and morphology of the printed scaffolds were analyzed by Fourier-Transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and microcomputed tomography (μCT). Attachment, proliferation and osteogenic differentiation of rat bone marrow stromal cells (BMSC) cultured on the printed scaffolds were…

Various 3D printing techniques currently use degradable polymers such as aliphatic polyesters to create well-defined scaffolds. Even though degradable polymers are influenced by the printing process, and this subsequently affects the mechanical properties and degradation profile, degradation of the polymer during the process is not often considered. Degradable scaffolds are today printed and cell–material interactions evaluated without considering the fact that the polymer change while printing the scaffold. Our methodology herein was to vary the printing parameters such as temperature, pressure, and speed to define the relationship between printability, polymer microstructure, composition, degradation profile during the process, and rheological behavior….

3D printed polycaprolactone (PCL) has potential as a scaffold for bone tissue engineering, but the hydrophobic surface may hinder optimal cell responses. The surface properties can be improved by coating the scaffold with cellulose nanofibrils material (CNF), a multiscale hydrophilic biocompatible biomaterial derived from wood. In this study, human bone marrow-derived mesenchymal stem cells were cultured on tissue culture plates (TCP) and 3D printed PCL scaffolds coated with CNF. Cellular responses to the surfaces (viability, attachment, proliferation, and osteogenic differentiation) were documented. CNF significantly enhanced the hydrophilic properties of PCL scaffolds and promoted protein adsorption. Live/dead staining and lactate dehydrogenase…

The mechanical properties of amorphous, degradable, and highly porous poly(lactide-co-caprolactone) structures have been improved by using a 3D fiber deposition (3DF) method. Two designs of 3DF scaffolds, with 45° and 90° layer rotation, were printed and compared with scaffolds produced by a salt-leaching method. The scaffolds had a porosity range from 64% to 82% and a high interconnectivity, measured by micro-computer tomography. The 3DF scaffolds had 8–9 times higher compressive stiffness and 3–5 times higher tensile stiffness than the salt-leached scaffolds. There was a distinct decrease in the molecular weight during printing as a consequence of the high temperature. The…