A facile one-step printing process by 3D micro-extrusion affording binder-free thermally reduced graphene oxide (TRGO) based electrochemical capacitors (ECs) that display high-rate performance is presented. Key intermediates are binder-free TRGO dispersion printing inks with concentrations up to 15 g L−1. This versatile printing technique enables easy fabrication of EC electrodes, useful in both aqueous and non-aqueous electrolyte systems. The as-prepared TRGO material with high specific surface area (SSA) of 593 m2 g−1 and good electrical conductivity of ≈16 S cm−1 exhibits impressive charge storage performances. At 100 and 120 Hz, ECs fabricated with TRGO show time constants of 2.5 ms…
In a versatile modular scaffold system, gradient nonwovens of in situ crosslinked gelatin nanofibers (CGN), fabricated by reactive electrospinning, are laminated with perforated layers and nonwovens of thermoplastic non-crosslinked biodegradable polyesters. The addition of glyoxal to a gelatin solution in a non-toxic solvent mixture consisting of acetic acid, ethyl acetate, and water (5:3:2 w/w/w) enables the in situ crosslinking of gelatin nanofibers during electrospinning. The use of this fluorine-free crosslinking system eliminates the need of post-treatment crosslinking and purification steps typical for conventional CGN scaffolds. The slowly progressing crosslinking of the dissolved gelatin in the presence of glyoxal increases the…
A novel and highly versatile synthetic route for the production of functionalized graphene dispersions in water, acetone, and isopropanol (IPA), which exhibit long-term stability and are easy to scale up, is reported. Both graphene functionalization (wherein the oxygen content can be varied from 4 to 16 wt%) and dispersion are achieved by the thermal reduction of graphite oxide, followed by a high-pressure homogenization (HPH) process. For the first time, binders, dispersing agents, and reducing agents are not required to produce either dilute or highly concentrated dispersions of single graphene sheets with a graphene content of up to 15 g L−1….
In this study we examined the release kinetics of valproate from polycaprolactone (PCL) implants constructed for local antiepileptic therapy. The PCL implants were produced with a novel 3D-Bioplotting technology. Release kinetics were determined by superfusion of these implants. Valproate was measured in the superfusate fractions with high pressure liquid chromatography (HPLC). The HPLC measurements were linear over a concentration range of 10-500 g/mL for valproate and the limit of quantification was found to be 9 g/mL. The HPLC method used is simple, accurate and sensitive. Within the first day, valproate (10%w/w)-PCL implants released already 77% of the maximum possible liberated…